HighTemperatures 3-Layer (3LPP) Heat-Shrinkable Tubular Sleeve (FJC 14D) (ISO21809-3)

3LPP 120C HSS Heat Shrink Coating System

(Open type sleeves with closure patch)

Technical Data Sheet

System Description

The pipeline 3 LPP 120C heat shrink coating system designed for corrosion protection of high temperature of straight pipes, fittings, bends, elbows and other irregular configurations, designed for a three layer field joint coating system for polypropylene coated pipeline and a three layer bend coating.

It consists thermoplastic hybrid adhesive and thick-wall irradiated cross linked polypropylene. When heated the backing layer shrinks and the adhesive flows and forms a reliable corrosion protection seal onto metal and adjacent coating surfaces.

Epoxy primer is a specially formulated 100% volume solid (solvent less) high temperature two component epoxy.

Product Features

●　High Temperature thermal - deformation

●　High Lap Shear Strength for High temperature

●　Excellent resistance to cathodic disbondment.

●　Long term corrosion protection.

●　Non hardening and non crackin for long term

●　Fast application and high performance.

●　Excellent chemical resistance

●　Excellent resistance to shear forces

●　Mechanical protection and moisture resistance.

Technical

Item	Test items	Test standard	Unit	3LPP 120C
Configuration	Operating Temperature	-	℃	Up to 120
	Liquid epoxy (heat cured)	ASTM D 1000	μm	≥200
	Polypropylene adhesive layer	ASTM D 1000	mm	≥0.8
	Polypropylene outer sheath layer	ASTM D 1000	mm	≥1.2
	Sleeve width	ASTM D 1000	mm	150-600
	Total thickness	ASTM D 1000	mm	2.0-3.0
Adhesive	Thickness as supplied	ASTM D 1000	mm	≥ 0.8
	Density	ASTM D792	kg/dm3	0.89-0.99
	Melting point	ASTM D3418	℃	130~140
	Lap Shear, at 23±2℃	EN 12068	N/cm	≥500
	Lap Shear, at 120±2°C	EN 12068	N/cm	≥10
Backing (PP)	Density	ASTM D792	kg/dm3	0.89-0.99
	Tensile Strength, at 23±2℃	ASTM D638	MPa	≥25
	Elongation, at 23±2℃	ASTM D638	%	≥300
	Hardness	ISO 868	Shore D	≥.65
	Water Absorption,per 24 hrs	ASTM D570	%	<0.5
	Dielectric Strength	ASTM D149	kV/mm	≥25
	Melting point	ISO 3146	℃	≥150
	UV Resistance	EN12068,Annex F ISO 4892-2 DIN 30670	-	According to standard
	Brittleness temperature	ASTM D 746	℃	＜-20
	Volume Resisitivity	ASTM D 257	Ω.m	2.0X1015

Product Selection

Model: 3LPP 120C HSS-W Φ457*2.0-450 3LPP 120C: Backing PP Operating Temperature 120℃ HSS-W: Heat Shrinkable Wraparound Sleeves Φ457------Joint or Pipeline Dimete 2.0---------Thickness 450--------Roll Width (as supplied)
No.	Pipe Diameter mm	Total thickness mm	Backing mm	Adhesive mm	Width mm	Length mm
1	108	2.0 2.2 2.5 2.7 3.0	1.2 1.5 1.8 2.0	0.8 1.0 1.2 1.5 2.0 3.0	150 300 400 450 500 520 600	463
2	114					483
3	133					547
4	159					634
5	168					664
6	219					836
7	273					1017
8	323					1205
9	325					1212
10	355					1313
11	377					1387
12	406					1484
13	426					1551
14	457					1655
15	478					1897
16	508					1998
17	529					2169
18	559					2237
19	610					2337
20	630					2489
No.	Pipe Diameter mm	Total thickness mm	Backing mm	Adhesive mm	Width mm	Length mm
21	660	2.0 2.2 2.5 2.7 3.0	1.2 1.5 1.8 2.0	0.8 1.0 1.2 1.5 2.0 3.0	150 300 400 450 500 520 600	2519
22	711					2660
23	720					2832
24	762					3003
25	813					3171
26	864					3342
27	914					3514
28	965					3685
29	1016					1897
30	1067					1998
31	1118					3856
32	1168					4024
33	1219					4196
34	1321					4538
35	1422					4878
36	1524					5220
37	1626					5563
38	1727					5902
39	1829					6245
40	1930					6584
41	2032					6927
42	2440					8298
43	2600					8835
44	3000					10179
45	3620					12262
46	4852					16402